Resin/Hardener Kit, A/B, Gallon
White Room Temperature Epoxy Laminating Resin
DESCRIPTION
PT2114 is a room temperature curing laminating resin for the construction of very stable tooling. PT2114 has excellent fabric penetration capabilities for easy, labor saving use. It exhibits minimum drain on vertical surfaces, which works well on multiple contoured configurations. Two hardeners are available for use with PT2114 resin for different sized laminates. Both offer similar handling properties and excellent cured physicals.
PT2114 has seen wide usage in applications such as:
Hammer Forms Assembly Fixtures Drill Fixtures
Master Gages Checking Fixtures Checking Gages
Duplicating Masters Sandwich Panels Prototype Fabrications
High Strength Laminated Tooling
|
|
PT2114-A |
PT2114-B |
PT2114-B1 |
ASTM Method |
|
Color |
White |
Amber |
Amber |
Visual |
|
Viscosity |
4,000 cps |
800 cps |
500 cps |
D2392 |
|
Specific Gravity, gms./cc |
1.3 |
1.02 |
1.01 |
D1475 |
|
Mix Ratio |
- - - - - |
100 : 18 By Weight |
100 : 18 By Weight |
|
|
Pot Life,4 fl.oz.Mass @ 77ºF |
- - - - - |
30 min. |
50 - 60 min. |
D2471 |
HANDLING and CURING
Both PT2114 hardeners will provide good cures at ambient temperatures. With PT2114 Part B, a room temperature cure of 18 to 24 hours, depending upon shop temperatures, is sufficient to allow handling of the laminate. When using PT2114 Part B1, particularly in colder temperatures, at least 24 hours cure will be required to develop good properties. Full cure can be accelerated by 1 to 2 hours at 150oF after an overnight cure at ambient temperature. Heat curing will usually increase shrinkage somewhat, so care should be taken to control the heat.
Product Description
Resin/Hardener Kit, A/B, Gallon
White Room Temperature Epoxy Laminating Resin
DESCRIPTION
PT2114 is a room temperature curing laminating resin for the construction of very stable tooling. PT2114 has excellent fabric penetration capabilities for easy, labor saving use. It exhibits minimum drain on vertical surfaces, which works well on multiple contoured configurations. Two hardeners are available for use with PT2114 resin for different sized laminates. Both offer similar handling properties and excellent cured physicals.
PT2114 has seen wide usage in applications such as:
Hammer Forms Assembly Fixtures Drill Fixtures
Master Gages Checking Fixtures Checking Gages
Duplicating Masters Sandwich Panels Prototype Fabrications
High Strength Laminated Tooling
|
|
PT2114-A |
PT2114-B |
PT2114-B1 |
ASTM Method |
|
Color |
White |
Amber |
Amber |
Visual |
|
Viscosity |
4,000 cps |
800 cps |
500 cps |
D2392 |
|
Specific Gravity, gms./cc |
1.3 |
1.02 |
1.01 |
D1475 |
|
Mix Ratio |
- - - - - |
100 : 18 By Weight |
100 : 18 By Weight |
|
|
Pot Life,4 fl.oz.Mass @ 77ºF |
- - - - - |
30 min. |
50 - 60 min. |
D2471 |
HANDLING and CURING
Both PT2114 hardeners will provide good cures at ambient temperatures. With PT2114 Part B, a room temperature cure of 18 to 24 hours, depending upon shop temperatures, is sufficient to allow handling of the laminate. When using PT2114 Part B1, particularly in colder temperatures, at least 24 hours cure will be required to develop good properties. Full cure can be accelerated by 1 to 2 hours at 150oF after an overnight cure at ambient temperature. Heat curing will usually increase shrinkage somewhat, so care should be taken to control the heat.
Product Videos
Custom Field
White Room Temperature Epoxy Laminating Resin
DESCRIPTION
PT2114 is a room temperature curing laminating resin for the construction of very stable tooling. PT2114 has excellent fabric penetration capabilities for easy, labor saving use. It exhibits minimum drain on vertical surfaces, which works well on multiple contoured configurations. Two hardeners are available for use with PT2114 resin for different sized laminates. Both offer similar handling properties and excellent cured physicals.
PT2114 has seen wide usage in applications such as:
Hammer Forms Assembly Fixtures Drill Fixtures
Master Gages Checking Fixtures Checking Gages
Duplicating Masters Sandwich Panels Prototype Fabrications
High Strength Laminated Tooling
|
|
PT2114-A |
PT2114-B |
PT2114-B1 |
ASTM Method |
|
Color |
White |
Amber |
Amber |
Visual |
|
Viscosity |
4,000 cps |
800 cps |
500 cps |
D2392 |
|
Specific Gravity, gms./cc |
1.3 |
1.02 |
1.01 |
D1475 |
|
Mix Ratio |
- - - - - |
100 : 18 By Weight |
100 : 18 By Weight |
|
|
Pot Life,4 fl.oz.Mass @ 77ºF |
- - - - - |
30 min. |
50 - 60 min. |
D2471 |
HANDLING and CURING
Both PT2114 hardeners will provide good cures at ambient temperatures. With PT2114 Part B, a room temperature cure of 18 to 24 hours, depending upon shop temperatures, is sufficient to allow handling of the laminate. When using PT2114 Part B1, particularly in colder temperatures, at least 24 hours cure will be required to develop good properties. Full cure can be accelerated by 1 to 2 hours at 150oF after an overnight cure at ambient temperature. Heat curing will usually increase shrinkage somewhat, so care should be taken to control the heat.